The Encapsulation of Illite Powders with Al2(SO4)3·18H2O and Hydrophilic Copolymers: Accelerating and Toughening Cement Hydration Through the Proliferation of 54CaO·MgO·Al2O3·16SiO2 Clinker

Nanomaterials, Год журнала: 2025, Номер 15(4), С. 283 - 283

Опубликована: Фев. 13, 2025

Two hydrophilic copolymers containing functional groups such as carboxyl, amido, and sulfonic acid are synthesized using ammonium persulfate-catalyzed free radical polymerization in water. Aluminum sulfate is then introduced, resulting two polymer complexes that exhibit reduced cement setting times (initial, 1.16-2.44 min; final, 2.02-3.14 min) improved compressive (24 h, 5.81-7.25 MPa) flexural 2.80-2.99 strengths compared to pure aluminum sulfate-facilitated cementing 19.11 37.05 compressive, 24 5.51 MPa; flexural, 2.56 MPa). Following this, ball-milled illite powder added, the admixtures further display slightly prolonged 2.35-2.99 vs. 3.98-4.35 min), along with comparable (5.85-7.11 enhanced (3.92-5.83 Notably, a unique adhesive pozzolanic clinker, Ca54MgAl2Si16O90 (54CaO·MgO·Al2O3·16SiO2), emerges presence of illite-based admixtures, contributing mechanical strength development hydrated mortars. Although itself hydrophobic, coating facilitates its dispersion into gaps pores matrix during setting, thereby increasing strength. This work presents an interesting approach utilizing materials applications, which significant for reducing CO2 emissions production use.

Язык: Английский

---

Synthesis, crystal structure, Hirshfeld surface analysis, molecular docking and DFT investigations of the anti-COVID-19 drug Ensitrelvir

Journal of Molecular Structure, Год журнала: 2025, Номер unknown, С. 142359 - 142359

Опубликована: Апрель 1, 2025

Язык: Английский

---

Design of hydrogen bond liquid crystals towards various electronic applications

Journal of Molecular Liquids, Год журнала: 2024, Номер 408, С. 125189 - 125189

Опубликована: Июнь 5, 2024

Язык: Английский

---

Novel Strategy of Treating 2-Nitrobenzoic Acid Crystals with Energetic N2 Neutrals Using Cold Plasma

Processes, Год журнала: 2024, Номер 12(11), С. 2336 - 2336

Опубликована: Окт. 24, 2024

The organic adduct compounds of 2-nitrobenzoic acid crystals were grown as optically transparent using the conventional slow evaporation solution technique. powdered and irradiated with cold plasma. Cell parameter analysis confirmed formation a new crystalline material that resides in triclinic P crystal system space group P1. Fourier transform infrared spectra recorded KBr pellet technique to determine vibrational functional groups compound. Powder X-ray diffraction was used reveal orientation samples crystals. obtained full width at half maximum for (001) plane XRD spectrum indicates excellent quality UV–Vis absorption possess cut-off edges wavelengths 428 nm 353 354 pure plasma-treated samples, respectively. optical energy bandgaps found be 2.0, 2.25, 4.06, 4.02 eV photoluminescence show blue emissions crystal. FE-SEM images morphological modifications which rounded platelets appear on surfaces treated

Язык: Английский

---

The Efficient and Environmentally Friendly Chlorination of Arene, Alcohol, Halobenzene, and Peroxide Catalyzed by Fe–Ba Binary Oxides Using Hydrochloric Acid as Chlorine Source and Aqueous H2O2 as Oxidant

Molecules, Год журнала: 2024, Номер 29(22), С. 5451 - 5451

Опубликована: Ноя. 19, 2024

A series of Fe-Ba mixed oxides, including a pure Fe-containing sample as reference, have been synthesized via sol-gel process using Fe

Язык: Английский

---