Performance of CO<sub>2 </sub>Adsorption on Modified Activated Carbons Derived from Okara Powder Waste: Impacts of Ammonia Impregnation DOI Open Access
Tuan‐Dung Hoang,

Dung Duc Le,

Minh Thang Le

и другие.

Опубликована: Авг. 13, 2024

The activated carbons (ACs) derived from okara powder waste with high surface areas were modified ammonia aqueous solution impregnation in an autoclave to enhance their CO2 adsorption properties toward CO2. impregnated ACs characterized which chemical composition and of the analyzed by SEM-EDS, FTIR. Activated functionalized (25%) through a hydrothermal process within 24; 48, 72 hours. performance onto carbon samples was experimentally evaluated breakthrough experimental setup at room temperature. FTIR spectra confirm N-containing N-modified presence –C = O stretch N-H groups. uptakes are 0.24; 1.47; 1.20 mmol/g, relatively comparable those studied literature.

Язык: Английский

Performance of CO<sub>2 </sub>Adsorption on Modified Activated Carbons Derived from Okara Powder Waste: Impacts of Ammonia Impregnation DOI Open Access
Tuan‐Dung Hoang,

Dung Duc Le,

Minh Thang Le

и другие.

Опубликована: Авг. 13, 2024

The activated carbons (ACs) derived from okara powder waste with high surface areas were modified ammonia aqueous solution impregnation in an autoclave to enhance their CO2 adsorption properties toward CO2. impregnated ACs characterized which chemical composition and of the analyzed by SEM-EDS, FTIR. Activated functionalized (25%) through a hydrothermal process within 24; 48, 72 hours. performance onto carbon samples was experimentally evaluated breakthrough experimental setup at room temperature. FTIR spectra confirm N-containing N-modified presence –C = O stretch N-H groups. uptakes are 0.24; 1.47; 1.20 mmol/g, relatively comparable those studied literature.

Язык: Английский

Процитировано

1