Extraction and physical characterization of Nymphaea Rubra (water lily) cellulosic fiber for potential textile and green-composite application

International Journal of Biological Macromolecules, Год журнала: 2025, Номер unknown, С. 141145 - 141145

Опубликована: Фев. 1, 2025

Язык: Английский

---

From plant to product: investigation of a cellulosic fiber from Xanthium strumarium L. subsp. strumarium stem for its potential use in composite applications

Biomass Conversion and Biorefinery, Год журнала: 2025, Номер unknown

Опубликована: Фев. 27, 2025

Язык: Английский

---

A comprehensive review of natural fiber reinforced Polymer composites as emerging materials for sustainable applications

Applied Materials Today, Год журнала: 2025, Номер 43, С. 102666 - 102666

Опубликована: Март 5, 2025

Язык: Английский

---

Evaluation and comparison of the behavioral properties of raw, alkali-treated, and triethoxy silane–treated cellulosic fibers derived from Rottboellia cochinchinensis plant as a substantial material for polymer composites

International Journal of Biological Macromolecules, Год журнала: 2025, Номер unknown, С. 142794 - 142794

Опубликована: Апрель 1, 2025

Язык: Английский

---

Characterization of novel fibers extracted from Rumex obtusifolius L. plant for potential composite applications

Materials Testing, Год журнала: 2025, Номер unknown

Опубликована: Апрель 11, 2025

Abstract In this study novel natural fibers were extracted from Rumex obtusifolius L. Extracted dried for further analysis. The chemical composition was analyzed, revealing the following fiber contents: cellulose at 63.52 ± 1.51 %, hemicellulose 27.15 0.72 and lignin 9.35 0.57 %. Thermal behavior of investigated by using thermogravimetric derivative analyses (TG DTG) it found that thermally stable up to 237.55 °C (T onset ) maximum degradation temperature max determined as 354.67 °C. Fiber diameter varied in range 226–539 µm density measured 1.12 0.74 g cm −3 . crystalline structure examined through X-ray diffraction (XRD) analysis, crystallinity index (CI) crystallite size (CS) based on corresponding patterns. CI CS values 69.81 % 3.08 nm, respectively. mechanical properties evaluated a single tensile testing method. strength, elastic modulus, strain break 192.81 43.33 MPa, 14.56 3.27 GPa, 1.45 0.43 Result showed R. are suitable composite applications reinforcement material.

Язык: Английский

---

Characterization of Waste Nicotiana rustica L. (Tobacco) Fiber Having a Potential in Textile and Composite Applications

Polymers, Год журнала: 2024, Номер 16(8), С. 1117 - 1117

Опубликована: Апрель 17, 2024

L. (NRL) is a type of tobacco plant, and its stalk waste potential lignocellulosic source for obtaining cellulose fibers freely available in nature. However, they are left fields after harvesting, this study provides green sustainable method to reuse waste. Fiber was obtained by retting the plant stalks water decomposing them naturally three weeks. NRL fiber characterized comparing it with known bast fibers, tests were applied examine physical, chemical, mechanical, morphological, thermal properties. With high content (56.6 wt%), had tensile strength (113.4 MPa) good crystallinity index (70%) that helped bond other composite matrix. Furthermore, an environmentally friendly alternative synthetic diameter 36.88 μm low density (1.5 g/cm

Язык: Английский

---

Physiochemical profiling of bioplasticizer derived from Ficus benghalensis leaves for eco-friendly applications

Industrial Crops and Products, Год журнала: 2024, Номер 222, С. 119535 - 119535

Опубликована: Авг. 31, 2024

Язык: Английский

---