Corrosion Behavior of 110SS Steel in Self‐Generated Acid at High Temperature DOI Open Access
Juan Du,

Qichao Zou,

Pengfei Chen

и другие.

Materials and Corrosion, Год журнала: 2024, Номер unknown

Опубликована: Дек. 25, 2024

ABSTRACT The corrosion behavior of hydrogen sulfide corrosion‐resistant alloy steel 110SS in the self‐generated acid system at (ultra‐) high temperature was studied. results weight loss experiment showed that rate decreased with increase 120°C–200°C. comprehensive study SEM‐EDS and XPS FeCO 3 formed on surface steel. With temperature, became dense, decreased. In addition, when is 120°C, 3D laser scanning show strong, phenomenon inhibited after adding oleic imidazoline. SEM electrochemical experiments imidazoline inhibitor can be stably adsorbed reduce its acid.

Язык: Английский

Investigation of Friction and Erosion Wear Properties of Titanium and Titanium Alloy Pipes DOI Open Access

Ting Mao,

Zhiming Yu,

Jing Yan

и другие.

Materials, Год журнала: 2024, Номер 17(20), С. 5043 - 5043

Опубликована: Окт. 15, 2024

Titanium alloys are applied in oil and gas development transportation to improve conditions because of their high specific strength corrosion resistance. However, the disadvantage poor wear resistance has become an obstacle developing titanium alloys. The friction properties pure TA3 alloy TA10 were tested under different loads forms using a reciprocating tester. Moreover, erosion was studied gas–solid results show that rate increases with increasing load. Under load 50 N, mass losses dry wet 0.0013 g 0.0045 g, respectively, while 0.0033 0.0046 respectively. While increased 70 loss even greater, reaching 0.0065 0.0058 g. include abrasive wear, adhesive oxidation wear. joint action various leads materials. simulated working conditions, rates 1.01 × 10−3 g/s 0.94 g/s. mechanism is same, including plowing, indentation cracking.

Язык: Английский

Процитировано

3

The corrosion behavior and passive film structure of industrial pure titanium with different Fe content in hydrochloric acid DOI Creative Commons

Xingyu Ouyang,

Yu Yang, Wenjun Ye

и другие.

Journal of Materials Research and Technology, Год журнала: 2025, Номер 35, С. 599 - 610

Опубликована: Янв. 10, 2025

Язык: Английский

Процитировано

0

Evaluation of Niobium-Based Bipolar Plates with Ultra-Low Precious Metal Coatings for High-Performance and Durable PEM Water Electrolyzers DOI Creative Commons
Yasin Mehdizadeh Chellehbari,

Leila Moradizadeh,

Mohammadhossein Johar

и другие.

Materials Today Energy, Год журнала: 2025, Номер unknown, С. 101913 - 101913

Опубликована: Май 1, 2025

Язык: Английский

Процитировано

0

Effect of Heat Treatment Temperature on the Microstructure and Properties of Titanium-Clad Steel Plate Prepared by Vacuum Hot Rolling DOI Open Access
Juan Pu,

Tingmu Chen,

Yubo Sun

и другие.

Coatings, Год журнала: 2024, Номер 14(9), С. 1096 - 1096

Опубликована: Авг. 30, 2024

Titanium-clad steel plates are widely used in chemical equipment and nuclear power due to their excellent corrosion resistance high strength. However, the Ti-C Fe-Ti compounds generated easily at titanium/steel interface deteriorate bonding strength of titanium steel, especially high-temperature service environments. In this study, pure Fe DT4 was chosen as an intermediate layer control formation interfacial compounds. The titanium/DT4/steel were manufactured by hot rolling technology with a small hole vacuuming. Then, titanium-clad annealed temperatures 450 °C, 550 650 °C modify microstructure properties. composition, mechanical properties plates, property studied as-rolled state under different annealing temperatures. results showed that TiC, FeTi, Fe2Ti state. After treatment, types quantities reduced, these mainly TiC FeTi temperature °C. compound only appeared variation determined hardness shear plates. more compounds, higher lower Therefore, when lowest highest. Meanwhile, significant improvement, indicating provides favorable conditions for enhancing performance plate.

Язык: Английский

Процитировано

2

Effect of Temperature on Thermal Oxidation Behavior of Ti-6Al-4V ELI Alloy DOI Open Access
Krzysztof Aniołek, Adrian Barylski,

Jan Rak

и другие.

Materials, Год журнала: 2024, Номер 17(16), С. 4129 - 4129

Опубликована: Авг. 20, 2024

In this paper, the morphological, micromechanical and tribological characteristics of Ti-6Al-4V ELI alloy after thermal oxidation (TO) were identified. TO was carried out at temperatures 848 K, 898 K 948 over a period 50 h. Microscopic examination revealed that an increase in temperature resulted improved uniformity coverage increased oxide grain size. Micromechanical tests showed led to hardness deformation resistance. Following oxidation, decrease (by approximately 10–22%) observed total mechanical work indentation, Wtotal, compared as-received material. The formation protective films on also improvement characteristics, both when tested under dry friction conditions Ringer’s solution. sliding wear resistance with temperature. However, greater degree reduction 30–50%) found for lubricated contact comparison tests. Surface roughness

Язык: Английский

Процитировано

1

The corrosion behavior of Ti-6Al-4Zr-3Nb-1.1Mo-1Sn-1V alloy pipes in hydrochloric acid solution DOI
Chengliang Mao,

Weiju Jia,

Qian Li

и другие.

Materials Today Communications, Год журнала: 2024, Номер unknown, С. 111261 - 111261

Опубликована: Дек. 1, 2024

Язык: Английский

Процитировано

1

Corrosion Behavior of 110SS Steel in Self‐Generated Acid at High Temperature DOI Open Access
Juan Du,

Qichao Zou,

Pengfei Chen

и другие.

Materials and Corrosion, Год журнала: 2024, Номер unknown

Опубликована: Дек. 25, 2024

ABSTRACT The corrosion behavior of hydrogen sulfide corrosion‐resistant alloy steel 110SS in the self‐generated acid system at (ultra‐) high temperature was studied. results weight loss experiment showed that rate decreased with increase 120°C–200°C. comprehensive study SEM‐EDS and XPS FeCO 3 formed on surface steel. With temperature, became dense, decreased. In addition, when is 120°C, 3D laser scanning show strong, phenomenon inhibited after adding oleic imidazoline. SEM electrochemical experiments imidazoline inhibitor can be stably adsorbed reduce its acid.